为什么导热界面材料的热阻和导热系数的测试多选择ASTM D5470作为标准？
热界面材料（英语：Thermal Interface Material）是用于涂敷在散热器件与发热器件之间，降低它们之间接触热阻所使用的材料的总称。南京睿公司提供美国第三方实验室的ASTM D5470热阻和导热系数检测报告。咨询电话：025-86583475
Thermal Interface Materials (TIM): Thermal Conductivity Testing ASTM D5470
An often used technique for thermal conductivity testing is the absolute steady-state technology with a guarded-hot-plate based on ASTM C177 or ISO 8302. Within this method, a sample is heated by a heat-source with a known steady-state power input and the resulting temperature drop across a given length is measured via thermocouples. The challenge of this technology is to minimize parasitic heat losses to a very low level and overcome the influences of contact resistance between sample an metal bars. The steady-state method from ASTM C177 and ISO8302 is adapted for thermal interface materials in the standard ASTM D5470.
导热界面材料ASTM D5470导热系数测试方法
ASTM D5470标准是基于理想化的热条件。将给定厚度的测试样品置于两热等温的平行表面之间，热梯度通过两 接触面的温度差施加在试样上，导致热流从试样中通过。热流垂直且均衡的穿过测试表面，同时确保无横向热传输。ASTM D5470标准用于测试处于稳态的电绝缘材料的热阻抗，用于测试以下几大类材料：在受到应力后显示无限变形的粘性液体，如 ：硅脂、相变材料、硬胶，这些材料不显示弹性特征，在移除应力后不会回复到原来的状态；粘弹性固体，形变应力始终与材料内部应力保持平衡，如凝胶、软质橡胶，这些材料显示出于材料厚度相关的线性弹性特征；微小变形的弹性固体，包括陶瓷 、金属及某些塑料。
界面接触热阻会存在于试样和测试界面之间，这些接触热阻很大程度上受试样的表面特性和测试界面施加在试样表 面的压力变化而变化。
测试设备要求，测试表面需要有0.4微米的粗糙度及5微米的平行度。加热器周围必须用高质量的绝缘材料进行保护 ，防止热流在通过测试试的时候泄露。
ASTM E1530热导测试 http://www.firete.com/popular_standards/9760.html
ASTM E1530 / ASTM D 5470 http://www.firete.com/popular_standards/9764.html
更多关于ASTM D5470、ASTM E1461,ASTM E1530等热阻和导热系数测试，请咨询南京睿督公司